- Name
- Sublimation residue made of mineral mixture (Magnetite 63wt%, NH4-nontronite 22wt%, Antigorite 9wt%, Dolomite 6wt%) at 173 K
- Database
- Experimentalists
- Date
- 2019-04-28
- Thickness
- 0.9 $\pm$ 0.1 $mm$
- Diameter
- 48.0 $mm$
- Surface roughness
- sligthly rough
- Substrate material
- black aluminum tape
- Substrate comments
- Cylindrical container of 4.8 cm diameter and 2.0 cm depth, which had been coated with black matte aluminum tape on the inside.
- Comments
- The thickness of the dry sublimation residue was measured with a ruler to be slightly less than 1 mm.
The sample resulting from the sublimation experiment has been carefully taken out of the cell, and cut to adjust to the size of the sample holder. Maximum care was taken to keep the physical structure of the sample.
- Temperature
- 173.0 $K$
- Temperature max
- 173.0 $K$
- Type
- vacuum
- Fluid pressure
- 1.5e-06 $mbar$
- Comments
- The sample was kept under high vacuum