- Title
- Mass abs. coef. (cm2/g) of glassy silicate grains MgO(1-x).SiO2(x), x=0.50, X50A, T=300K
- Database
- Experiment type
- laboratory measurement
- Spectrum type
- absorption coefficient
- Version
- #1 (2017-07-13 12:50:18 UTC+0000)
- Instrument
- vertex70v-transmission-MIR
- Spectral observation mode
- spectrum
- Valid spectral range(s)
- 250.0 - 2000.0 $cm^{-1}$
- Observation geometry
- direct :
- Angle observation mode
- fixed angles
- Spatial observation mode
- single spot
- Instrument
- vertex70v-transmission-FIR
- Spectral observation mode
- spectrum
- Valid spectral range(s)
- 10.0 - 300.0 $cm^{-1}$
- Observation geometry
- direct :
- Angle observation mode
- fixed angles
- Spatial observation mode
- single spot
- Instrument
- Brucker125V-transmission-FIR
- Spectral observation mode
- spectrum
- Valid spectral range(s)
- 10.0 - 40.0 $cm^{-1}$
- Observation geometry
- direct :
- Angle observation mode
- fixed angles
- Spatial observation mode
- single spot
- Name
- Glassy silicate (1-x)MgO-xSiO2, x=0.50, HDPE and KBr pellets
- Texture
- compact
- Thickness
- 2.0 $\pm$ 0.4 $mm$
- Temperature
- 300.0 $\pm$ 2.0 $K$
References
- Data reference
- Demyk, Karine; Meny, Claude; Lu, Xing-Heng (2015): Mass absorption coefficient spectra (cm2/g) of glassy MgO(1-x).SiO2(x), x=0.35, 0.40 and 0.50, at 10 to 300 K in the 5 - 1000 µm range. SSHADE/STOPCODA (OSUG Data Center). Dataset/Spectral Data. https://doi.org/10.26302/SSHADE/EXPERIMENT_KD_20170711